It is heated, thoroughly mixed, and used with a brush or spatula.
A depolarizing solution for use in zinc-carbon batteries like the Grenet is composed as follows:
Dissolve one pound of bichromate potash or soda in ten pounds of water (by weight). When it is thoroughly dissolved add two and one-half pounds of sulphuric acid, slowly pouring it into the bichromate solution and stirring it with a glass rod. The addition of the acid will heat the solution. Do not use it until it has entirely cooled.
To rub the edges of glass, such as the disks for Wimshurst machines, obtain a piece of hard sandstone, such as is used for sharpening knives or scythes. The glass is placed on a table so that the edge extends beyond. Oil of turpentine is rubbed or dropped on the surface of the stone, and the edge of the glass is moistened with a rag soaked in the turpentine. Hold the glass down securely with one hand, and with the other grasp the stone and give it a forward and backward motion, grinding the glass along its edge and not crosswise. With care and patience a rough edge can soon be brought to a smooth one, and a soft, rounded corner substituted for the hard, angular, cutting edge that makes the glass a difficult thing to handle. Use plenty of lubricant in the form of oil of turpentine to make the work easy.
One of the best glues for glass and wood or glass and fibre is made by placing some high-grade glue (either flake or granulated) in a cup or tin and covering it with cold water. Allow it to stand several hours until the glue absorbs all the water it will and becomes soft; then pour the water off, and add glacial acetic acid to cover the glue. The proportion should be eighteen parts of glue to two of acid. Heat the mass until it is reduced to liquid, stirring it until it is thoroughly mixed. When ready for use it should be poured into a bottle and well corked to keep the air away from it.
Apart from glass and porcelain, insulators can be made from non-conducting compounds, the best of which is molded mica. Ground mica or mica dust is mixed with thick shellac until it is in a putty-like state. It may then be forced into oiled molds of any desired shape. Hydraulic pressure is employed for almost every form of molded mica that is made for commercial purposes; but as a boy cannot employ that means to get the best results, he must use all the pressure that his hands and a flat board will give.